Calcium Aluminate Cement, High Aluminate Cement A600, A700.G9, CA-70, CA-80
Short Description
Features
Lower porosity,high chemical stability, high temperature performance,high wear resistance
Details information
The product is usually used as various kiln materials for metallurgy,petrochemical, petroleum, machinery,building materials and other industries.
High Alumina Cement CA-50
|
Items |
Unit | A600 | A700 | G9 | ||
| Chemical composition | Al2O3 | % | 50-60 | 50-60 |
53.5max |
|
| CaO | % | 33min | 33.00min |
33.00min |
||
| SiO2 | % | 8.00max | 8.00max |
5.50max |
||
| Fe2O3 | % | 2.50max | 2.50max |
2.50max |
||
| RO2 | % | 0.4max | 0.40max |
0.40max |
||
| Specific Surface Aea | cm3/g | 3000max | 3000max | 350min | ||
| Beginning Set | min | 60min | 60min |
90min |
||
| Ending Set | h | 6max | 6max |
6min |
||
| Bending Strength | 1 day | Mpa | 5.50max | 7.00min |
8.00min |
|
| 3 day | Mpa | 6.50max | 8.00min |
10.00min |
||
| Compressive Strength | 1 day | Mpa | 40.00max | 50.00min |
72.00min |
|
| 3 day | Mpa | 50.00max | 60.00min |
82.00min |
||
| Refractories | ℃ | 1350 | 1350 | 1450 | ||
Calcium Alumina Cement
|
Items |
Unit |
CA-70 | CA-80 | ||
| Chemical composition | Al2O3 | % | 68.50-72.00 | 78.50-81.00 | |
| CaO | % | 28.0-31.50 | 17.00-20.00 | ||
| SiO2 | % | ≤0.50 | ≤0.40 | ||
| Fe2O3 | % | ≤0.50 | ≤0.30 | ||
| K2O+Na2O | % | ≤0.50 | |||
| Specific Surface Aea | Cm2/g | ≥5000 | ≥7000 | ||
| Beginning Set | min | ≥45 | ≥30 | ||
| Ending Set | h | ≤6 | ≤6 | ||
| Bending Strength | 24h | Mpa | ≥7.0 | ≥5.50 | |
| Compressive
Strength |
24h | Mpa | ≥45 | ≥40 | |
| Refractories | ℃ | ≥1600 | ≥1790 | ||
-
Calcined Alumina Ultrafine For High-Performance...
-
Melt Drawn Heat Resistant Stainless Steel Fiber
-
Loose-Fill Refractories Alumina Bubble Is Used ...
-
Optimum Toughness Of The Grains Brown Fused Alu...
-
Semi-Friable Fused Alumina Widely Working On He...
-
Fused Silica Excellent Thermal And Chemical Pro...